ASTM A213 T22 Alloy Steel Pipe
ASTM A213 T22 seamless low-alloy (ferritic) steel pipe designed for boiler, superheater, and heat-exchanger applications. Suitable for elevated-temperature service with improved creep strength, oxidation resistance, and reliable mechanical performance.
Standard & Grade
- Standard: ASTM A213
- Grade: T22
- Product type: Seamless ferritic alloy steel pipe / tube
Applications
- Boilers
- Superheaters
- Heat exchangers
- High-temperature pressure systems
Manufacturing
- Manufactured by the seamless process
- Supplied either hot finished or cold finished, as specified
Heat Treatment
- Heat treatment performed separately and in addition to heating for hot forming
- Ferritic alloy steels reheated as required by specification
- Where applicable, rapid cooling or quenching may be applied after hot forming
Testing & Inspection
- Tension test
- Hardness test
- Flattening test
- Flaring test
- Each tube subjected to non-destructive electric testing or hydrostatic testing
Chemical Composition (Typical, %)
| Element | Value |
|---|---|
| UNS Designation | K21590 |
| Carbon | 0.05 – 0.15 |
| Manganese | 0.30 – 0.60 |
| Phosphorus (max) | 0.025 |
| Sulfur (max) | 0.025 |
| Silicon | 0.50 |
| Chromium | 1.90 – 2.60 |
| Molybdenum | 0.87 – 1.13 |
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength (min) | 415 MPa |
| Yield Strength (min) | 220 MPa |
| Elongation (min) | 30% |
Typical Size Range
- Inside Diameter: from 1/8 in. (3.2 mm)
- Outside Diameter: up to 5 in. (127 mm)
- Wall Thickness: 0.015 – 0.500 in. (0.4 – 12.7 mm)
- Other dimensions available on request
Delivery Condition
- Annealed